Novel polyisocyanurate catalysts

ABSTRACT

Polyisocyanurate catalysts are disclosed which have the formula: ##STR1## where R 1  and R 2  are independently selected from alkyl groups of less than about 3 carbon atoms or where R 1  and R 2  together comprise cycloalkyl or morpholino groups and where R 3  is hydrogen or alkyl groups containing less than about 3 carbon atoms. Said catalysts are useful in promoting the reaction between a polyol and an aromatic polyisocyanate to prepare a polymer containing recurring isocyanurate and urethane linkages.

This is a division of application Ser. No. 085,147, filed Oct. 15, 1979 now abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to the preparation of polyisocyanurate polymers such as polymer foams, and is more particularly concerned with use of a class of catalyst which promote the trimerization of polyisocyanates to polyisocyanurate polymers.

2. Description of the Prior Art

Polyisocyanurate polymers such as rigid polyisocyanurate foams are known in the art. The prior art discloses methods for preparing such polymers by reacting an organic polyisocyanate with a polyether or polyester polyol utilizing a polyisocyanurate group formation catalyst. Foams are prepared by effecting such reaction in the presence of a blowing agent. In the optimum situation the isocyanurate catalyst utilized promotes formation of both isocyanurate linkages and urethane linkages to produce urethane-modified polyisocyanurate polymers. See, for example, U.S. Pat. Nos. 3,516,950; 3,580,868; 3,620,986; 3,625,872; 3,635,848; 3,725,319; and 3,745,133.

Compounds which are known as catalysts for polyisocyanurates are the N-alkal metal and N-alkaline earth metal compounds of primary and secondary aliphatic, arylaliphatic, aromatic amines and heterocyclic amines. Amines which may be employed are, for example, methylamine, N-butylamine, tert.-butylamine, methoxy-n-propylamine, oleylamine, diethylamine, di-n-butylamine, diisobutylamine, dicyclohexylamine, N-methylstearylamine, benzylamine, ethylbenzylamine, dibenzylamine, phenylbenzylamine, aniline, naphthylamine, 3-N-ethylaminotoluene, toluidine, methylaniline, N-isobutylaniline, diphenylamine, N-methylanisidine, and also pyrrolidine, piperidine, 1,2,3,4-tetrahydroquinoline, pyrrole, indole, 2-methylindole, 2,3-dimethylindole, 5-methoxy-2,3-dimethylindole, carbazole, 3,6-dinitrocarbazole, N,N'-dimethylethylenediamine and N,N'-dimethyl-p-phenylenediamine.

N-alkali metal and N-alkaline earth metal compounds of carboxylic acid amides are also known catalysts. These include aliphatic and aromatic carboxylic acid amides and also such cyclic acid amides as imides and lactams. The following compounds are examples of compounds suitable for the production of such N-metal compounds: acetamide, trimethylacetamide, myristinic acid amide, stearoyl amid, N-methylacetamide, phenylacetamide, benzamide, N-alkyl benzamides, succinimide, tetrapropenyl succinimide, phthalimide, pyrrolidone, butyrolactam, caprolactam, phthalimidine and saccharine.

Also, as catalysts alkali or alkaline earth metal may be combined with the amines or carboxylic acid amides such as, for example, lithium, sodium, potassium, magnesium, barium, and calcium, with the preferred metals being lithium, sodium, potassium and calcium.

Also, alkali or alkaline earth metal salts of carboxylic acids are useful as catalysts for isocyanurate polymers.

The catalyst of this invention do not contain alkali or metals and provide an unexpected beneficial delay in the isocyanurate reaction which aids in processing. This delay is especially helpful where molding is undertaken. The catalyst herein also gives a complete product cure.

SUMMARY OF THE INVENTION

This invention comprises a novel process for preparing a polymer containing recurring isocyanurate and urethane linkages, which polymer comprises a reaction product of a polyol and an aromatic polyisocyanate utilizing as an isocyanurate formation catalyst a particularly useful and novel specific class of compounds known as falling within the formula: ##STR2## where R₁ and R₂ are independently selected from alkyl groups of less than about 3 carbon atoms or where R₁ and R₂ together comprise cycloalkyl or morpholino groups and where R₃ is hydrogen or alkyl groups containing less than about 3 carbon atoms. The invention is also the novel compositions described above.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The catalysts of the invention are useful as catalysts for the production of isocyanurate either used alone or in combination with other known catalysts. Compounds having the general formula depicted in the summary of the invention are included within the scope of our invention.

In a preferred embodiment R₁ and R₂ are alkyl groups having less than about 3 carbon atoms and R₃ is hydrogen.

In a particularly preferred embodiment R₁ and R₂ are methyl and R₃ is hydrogen and the catalyst has the formula:

    (CH.sub.3).sub.2 N--N═CH--CH.sub.2 OH                  (II)

and is called 1-(2,2-dimethylhydrazono)-2-hydroxyethane, also known as hydroxyacetaldehyde, 2,2-dimethylhydrazone.

Preparation of these materials can proceed as follows for example:

In order to obtain compound II, unsymmetrical methylhydrazine, (CH₃)₂ N--NH₂, is added to formaldehyde at a temperature from about -50° C. to 150° C. but preferably from about 0° C. and 80° C. at pressures ranging from about 0.01 atm to 200 atm but preferably at about one (1) atm. A solvent may be used but is not necessary. Suitable solvents water, alcohols and others.

If formaldehyde is added to unsymmetrical dimethylhydrazine instead of the reverse as above, 1-(2,2-dimethylhydrazino)-2-(2,2-dimethylhydrazono)ethane,

    (CH.sub.3).sub.2 N--NH--CH.sub.2 --CH═N--N(CH.sub.3).sub.2 (I)

is produced along with the 1-(2,2-dimethylhydrazono)-2-hydroxyethane.

The catalysts of this invention are surprisingly effective in catalyzing the isocyanurate reaction and provide a delayed reaction which is valuable for processing the foams. Furthermore, the catalysts of this invention are particularly advantageous in that they give a complete cure to the foam without other catalysts being present.

The Examples which follow depict the preparation of compounds I and II and the use of these materials as isocyanurate catalysts.

EXAMPLE I

To a 500 ml reactor equipped with a stirrer, thermometer, addition funnel and nitrogen atmosphere was charged 150 g unsym-dimethylhydrazine. With cooling to 5° C., 212 g formalin (37% formaldehyde) was added dropwise over 2 hours. After the addition, the reaction mixture was warmed to room temperature over 1.5 hours and water distilled under aspirator vacuum of 35 to 50 mm Hg. When about 150 ml remained a 12 inch distillation column was added and the distillation was continued. When ca. 30 ml remained, the column was removed and the remainder flash distilled; 21.6 g was collected bp₅₋₆ 65°-67° C. This final distillate was used as a catalyst to prepare an isocyanurate foam in Example II below.

EXAMPLE II

A foam was prepared by premixing the B-component ingredients listed below, and mixing the B-component on a high speed stirrer with 57.6 parts THANATE®P-270 polyisocyanate, and pouring the blend into a standard box mold and allowing the formulation to rise.

B-component ingredients:

25.9 parts Novolak polyol (OH No.=187, F=2.5)

0.5 parts DC-193 silicone surfactant

12 parts R-11B FREON® fluorocarbon

4 parts catalyst from Example 1

The foam rise characteristics are recorded below:

    ______________________________________                                         Cream time           22 seconds                                                Tack free time       60 seconds                                                Rise time            53 seconds                                                ______________________________________                                    

This formulation exhibits desirable rise characteristics for many isocyanurate foam applications in that it has a relatively long cream time and yet still has a reasonably short track free and rise time. This permits mold filling of the fluid blend and yet provides rapid cycle times for repetitive molding operations.

EXAMPLE III

This example is similar to Example I but the products are identified.

To a 1-l flask equipped with an additional funnel and stirrer and nitrogen atmosphere was charged 300 grams unsym.-dimethylhydrazine. After cooling to 7° C., 424 grams formalin was added dropwise over 2 hours with cooling and stirring. After standing at ambient temperature for 64 hours following addition, vacuum distillation was conducted and fraction A boiling at 74° C. (4-6 mm) and fraction B boiling at 73° C. (3 mm) were collected. Analysis of these fractions showed them to contain the following compounds:

Fraction A--contained a 1:1 molar ratio of compounds I and II.

Fraction B contained compound II.

Combined isolated yields of I and II were 1.72% and 4.7% respectively.

EXAMPLES IV AND V

Rigid urethane/isocyanurate foams were prepared from the compounds of Example III by a technique similar to that described in Example II.

    ______________________________________                                                           #4      #5                                                   ______________________________________                                         A Component                                                                    THANATE®P-270 isocyanate                                                                       58.3 parts                                                                               58.3 parts                                       B Component                                                                    Novolak polyol (OH No. 194, F 2.4)                                                                 25.2 parts                                                                               25.2 parts                                       DC-193 silicone surfactant                                                                         0.5 parts 0.5 parts                                        FREON®R-11B fluorocarbon                                                                       12 parts  12 parts                                         Catalyst - Example III, Fraction                                                                   4 parts   0 parts                                          Catalyst - Example III, Fraction B                                                                 0 parts   4 parts                                          Foam Cure Data                                                                 Cream time, sec.    4-5       18-20                                            Tack free time, sec.                                                                               28-30     60                                               Rise time, Sec.     45        105                                              ______________________________________                                    

Thus, compound I seems to be more active a catalyst providing a more rapid cure whereas compound II provides more of a delay.

EXAMPLE VI

To a nitrogen padded flask containing 81 g of formalin, 37% formaldehyde solution (1 mole), a stirrer, and thermometer was added 30 g unsym.-dimethylhydrazine dropwise over 110 minutes. The reaction solution was then warmed in a water bath 3 hours at temperatures not exceeding 44° C.

Gas liquid chromatographic analysis of the reaction mixture at this point revealed the presence of compound II. Although 33 g additional dimethylhydrazine was added and the temperature increased to 87° C. (reflux), none of compound I was detected and little additional II was formed.

Dimethylhydrazine and water were removed by heating the mixture at 60° C. while applying aspirator vaccum. The residue weighed 40 g and analysis showed it to be hydroxyacetaldehyde dimethylhydrazone (II). Both nmr and glpc analysis showed the product to be greater than 90% pure.

The next example illustrates the effectiveness of compound II as an isocyanurate catalyst in the absence of polyols.

EXAMPLE VII

To a nitrogen padded bottle containing 5.0 ml phenylisocyanate and 25 ml petroleum ether was added 2 drops of the catalyst of Example VI and 2 ml of allyl cyanide as a cosolvent. The bottle was sealed and allowed to stand at ambient temperature one hour. The solids which crystallized were filtered and washed pentane and reprecipitated from acetone/heptane. The crystals, 2.6 g, which were collected were identified as triphenylisocyanurate.

The following examples illustrate the comparison between the catalysts of this invention and commercially available amine based isocyanurate catalysts.

EXAMPLES VIII-XII

Foams were prepared by blending the A component and premixed B-components on a high speed stirrer.

    ______________________________________                                         Experiment Number                                                                               A       B       C     D                                       ______________________________________                                         A-Component (parts by wt.)                                                     MONDUR®MR    59      --      --    --                                      polyisocyanate                                                                 THANATE®P-270                                                                               --      60      56.6  58                                      polyisocyanate                                                                 B-Component (parts by wt.)                                                     Novolak based polyol                                                           (OH#194, F 2.4)  25.5    26      --    --                                      Novolak based polyol                                                           (OH#192, F 2.4)  --      --      24.9  25.5                                    DC-193 silicone surfactant                                                                       0.5    0.5      0.5   0.5                                    FRENON®R-11B fluorocarbon                                                  blowing agent    12      12      12    12                                      Catalyst from Example VI                                                                         5      --      --    --                                      50% potassium octoate in                                                       700 molecular wt. triol                                                                         --      1.5     --    --                                      DMP-30 (2,4,6-tris-(dimethyl-                                                  aminomethyl)phenol from                                                        Rohm and Haas    --      --       6    --                                      1,3,5-tris-(dimethylamino-                                                     propyl)hexahydrotriazine                                                                        --      --      --     4                                      Foam Cure Characteristics                                                      Cream time, sec. 13       4       4     5                                      Tack free time, sec.                                                                            59      45      55    35                                      Rise time, sec.  100     50      120   90                                      Comments about cured foam                                                                       Good    Good    Poor  Skin                                                                     exter-                                                                               cracks                                                                   nal   under                                                                    friabi-                                                                              slight                                                                   lity  pres-                                                                          sure                                    ______________________________________                                    

In comparison of the catalysts above, only the catalyst from Example VI gave a cream time delay. Other amine catalysts such as DMP-30 and 1,3,5-tris(dimethylaminopropyl)-hexahydro-1,3,5-triazine do not give good isocyanurate foams when used as the only catalyst. Alkali metal carboxylates give good foams but do not give the desired delay useful in many applications. Lower levels of alkali metals in formulations give incompletely cured foams. 

We claim:
 1. In a process for preparing a polymer containing recuring isocyanurate and urethane linkages, which polymer comprises the reaction product of a polyol and an aromatic polyisocyanate, while utilizing an isocyanurate group formation catalyst; the improvement which comprisesemploying as said isocyanurate catalyst a compound falling within the following structural formula: ##STR3## where R₁ and R₂ are independently selected from alkyl groups of less than about 3 carbon atoms or where R₁ and R₂ together comprise cycloalkyl or morpholino groups and where R₃ is hydrogen or alkyl groups containing less than about 3 carbon atoms.
 2. The process of claim 1 where said polyol is a polyether or polyester polyol.
 3. The process of claim 1 wherein said polymer is a cellular polymer obtained by reacting said polyols in said polyisocyanate in the presence of a blowing agent.
 4. The process of claim 3 wherein a rigid polyisocyanurate is produced.
 5. In a process for preparing a polymer containing recurring isocyanurate and urethane linkages, which polymer comprises the reaction product of a polyol and an aromatic polyisocyanate, while utilizing an isocyanurate group formation catalyst; the improvement which comprisesemploying as said isocyanurate catalyst 1-(2,2-dimethylhydrazono)-2-hydroxyethane.
 6. The process of claim 5 where said polyol is a polyether or polyester polyol.
 7. The process of claim 5 wherein said polymer is a cellular polymer obtained by reacting said polyols in said polyisocyanate in the presence of a blowing agent.
 8. The process of claim 5 wherein a rigid polyisocyanurate foam is produced. 